| Typical physical properties | |
 | |
| |
| Saturation polarization Js | 2,03 T |
| |
| |
| |
| Coercive field strength Hc | 5 A/m |
| |
| |
| |
| Curie temperature Tc 745 °C | 1345 °F |
| |
| |
| |
| Density Pm | 7,65 kg/dm3 |
| |
| |
| |
| Electrical resistivity Pe | 0,48 µΩm |
| |
| |
| |
| Ultimate tensile strength Rm | |
longitudinal in rolling direction
transverse to rolling direction | 330 - 370 MPa
390 - 420 MPa |
| |
| |
| |
| Yield point Rp 0,2 | |
longitudinal in rolling direction
transverse to rolling direction | 300 - 340 MPa
330 - 360 MPa |
| |
| |
| |
| Elongation A I=80 | |
longitudinal in rolling direction
transverse to rolling direction | 6 - 14 %
24 - 48 % |
| |
| |
| |
| Hardness | |
HRB 15T
HV 5 | 75 - 85
170 - 180 |
| |
| |
| |
| Stacking factor, thickness | |
0,23 mm
0,27 mm
0,30 mm
0,35 mm | 95,5 %
96,0 %
96,5 %
97,0 % |
| |
| |
| |